ABOUT INDEXING EDITORIAL BOARD ARCHIVES AUTHOR GUIDELINES SUBMIT PAPER AUTHOR'S SUBSCRIPTIONS AUTHOR'S PAGE CONTACT
Materiale Plastice
Cite as: Mater. Plast.
https://doi.org/10.37358/Mat.Plast.1964

OSIM Nr. R102356
ISSN Print 0025-5289
ISSN Online 2668-8220
Journal Metrics
* Impact factor 2019: 1.517
* 5-Year IF: 1.179
* CiteScore: 2.4
* H index: 22
Materiale Plastice - Latest Issue

Latest Issue >>>
ARCHIVES
   Volume 57, 2020
   Volume 56, 2019
   Volume 55, 2018
   Volume 54, 2017
   Volume 53, 2016
   Volume 52, 2015
   Volume 51, 2014
   Volume 50, 2013
   Volume 49, 2012
   Volume 48, 2011
   Volume 47, 2010
   Volume 46, 2009
   Volume 45, 2008
   Volume 44, 2007
   Volume 43, 2006
   Volume 42, 2005
   Volume 41, 2004
   Volume 40, 2003
 
<<<< back

Materiale Plastice (Mater. Plast.), Year 2015, Volume 52, Issue 1,





CLAUDIU-AUGUSTIN GHIORGHITA, FLORIN BUCATARIU, MARCELA MIHAI, ECATERINA STELA DRAGAN Polyelectrolyte Multilayers Composed of Chitosan and Poly(acrylic acid)II. Sorption/release of methylene blue


Abstract:
Chitosan (CHI) and poly(acrylic acid) (PAA) polyelectrolyte multilayers were constructed onto silica microparticles with particle diameter of 40 - 60 mm (Daisogel type). The multilayers were subject to two post-treatment strategies: (i) immersion in an aqueous solution with pH = 2.4 for 5 min, followed by immersion for 1 min in water and thermal treatment at 120oC for 60 min and (ii) cross-linking with glutaraldehyde for 60 min. The sorption properties for a cationic dye were investigated taking methylene blue (MB) as a model. The reusability of (CHI/PAA)n multilayers deposited onto Daisogel microparticles in the consecutive sorption/desorption cycles of MB was investigated as a function of the number of double layers and the post-treatment strategy. Keywords: polyelectrolyte multilayer; chitosan; poly(acrylic acid); methylene blue; silica



Issue: 2015 Volume 52, Issue 1
Pages:
Publication date: 2015/3/30
download pdf   Download Pdf Article
Creative Commons License
This article is published under the Creative Commons Attribution 4.0 International License