ABOUT INDEXING EDITORIAL BOARD ARCHIVES AUTHOR GUIDELINES SUBMIT PAPER NEWS, EVENTS AUTHOR'S PAGE CONTACT
Materiale Plastice
Cite as: Mater. Plast.
https://doi.org/10.37358/Mat.Plast.1964

OSIM Nr. R102356
ISSN Print 0025-5289
ISSN Online 2668-8220
Materiale Plastice - Latest Issue

Latest Issue >>>
ARCHIVES
   Volume 61, 2024
   Volume 60, 2023
   Volume 59, 2022
   Volume 58, 2021
   Volume 57, 2020
   Volume 56, 2019
   Volume 55, 2018
   Volume 54, 2017
   Volume 53, 2016
   Volume 52, 2015
   Volume 51, 2014
   Volume 50, 2013
   Volume 49, 2012
   Volume 48, 2011
   Volume 47, 2010
   Volume 46, 2009
   Volume 45, 2008
   Volume 44, 2007
   Volume 43, 2006
   Volume 42, 2005
   Volume 41, 2004
   Volume 40, 2003
 
<<<< back

Materiale Plastice (Mater. Plast.), Year 2003, Volume 40, Issue 1,



Gheorghe Rusu

The Anionic Copolymerization of e-Caprolactam with Laurolactam of Several Additives


Abstract:
This paper deals with synthesis and characterization of some copolyamides 6/12 obtained by rotational molding via activated anionic ring-opening copolymerization of e-caprolactam with laurolactam. Sodium bis<(2-metoxyetoxy)e-caprolactam> aluminate, as initiator and N,N’--bis-e-caprolactam, as activator were used. The initial mold temperature (initial polymerization temperature) was kept constant at 160oC. The incorporation of laurolactam into nylon 6 chain depresses both in the degree of crystallinity and the melting temperature of nylon 6/12 copolymers. The notched Izod impact strength of the copolymers increased as the laurolactam content was increased, while the flexural modulus and the water absorption decreased.


Keywords:
e-aprolactam; laurolactam; anionic copolymerization; copolyamide 6/2; rotational molding

Issue: 2003 Volume 40, Issue 1
Pages:
Creative Commons License
This article is published under the Creative Commons Attribution 4.0 International License


Downloads number: 0
<<<< back
 
  Search Authors
Crossref Member Badge
 DOI  logo
 Gold Open Access | Source=http://www.plos.org/  | Author=art designer at PLoS
Creative Commons License